Influence of dealloying solution on the microstructure of nanoporous copper through chemical dealloying of Al75Cu25 ribbons. Issue 19 (14th October 2020)

• Record Type: Journal Article
• Authors: Ma, Hailan; Zhao, Bingge; Ding, Kai; Zhang, Yuanheng; Wu, Guanzhi; Gao, Yulai
• Is Part Of: Journal of materials research. Volume 35:Issue 19(2020)
• Page Start: 2610
• Page End: 2619
• Publication Date: 2020-10-14
• Subjects: Al, -- alloy, -- porosity; Materials -- Research -- Periodicals; 620.1105
• DOI: 10.1557/jmr.2020.69
• Languages: English
• ISSNs: 0884-2914

Abstract

Abstract: Abstract : In this article, Al75 Cu25 (at.%) ribbons were dealloyed by HCl, H2 C2 O4, H3 PO4, and NaOH solutions, respectively, to prepare nanoporous copper (NPC). The dealloying behavior is varied with dealloying solutions, allowing modulating the microstructure and porosity of the NPC. Al75 Cu25 ribbons are fully dealloyed in HCl, H2 C2 O4, and NaOH solutions, whereas they are partially dealloyed in H3 PO4 solution. Except the NPC prepared in the NaOH solution, no obvious cracks are traced in other samples. The surface diffusivity ( D s ) of Cu atoms along the alloy/solution interfaces is varied with solutions, producing the NPC with different microstructure. NPC with higher specific surface area can be obtained by dealloying the Al75 Cu25 ribbons in the HCl solution. Compared with the dealloying in H2 C2 O4, H3 PO4, and NaOH solutions, the dealloying in 10 wt% HCl solution for 25 min at 90 ± 1 °C facilitates the best NPC in this work.