Effects of solute elements on hardening and microstructural evolution in neutron-irradiated and thermally-aged reactor pressure vessel model alloys. Issue 10 (2nd October 2016)

• Record Type: Journal Article
• Authors: Liu, Li; Nishida, Kenji; Dohi, Kenji; Nomoto, Akiyoshi; Soneda, Naoki; Murakami, Kenta; Li, Zhengcao; Chen, Dongyue; Sekimura, Naoto
• Is Part Of: Journal of nuclear science and technology. Volume 53:Issue 10(2016)
• Page Start: 1546
• Page End: 1553
• Publication Date: 2016-10-02
• Subjects: Neutron irradiation -- microstructure -- precipitation -- thermal ageing -- RPV model alloy; Nuclear engineering -- Periodicals; Nuclear physics -- Periodicals; Nuclear energy -- Periodicals; 621.4805
• DOI: 10.1080/00223131.2015.1136902
• Languages: English
• ISSNs: 0022-3131

Abstract

ABSTRACT: Nanometer-sized Cu-enriched solute clusters containing Mn, Ni, and Si atoms are considered as the primary embrittling feature in reactor pressure vessel steels. In order to understand the effects of solute atoms Mn, Ni, and Si on hardening and cluster formation, reactor pressure vessel model alloys FeCu, FeCuSi, FeCuNi, and FeCuNiMn were irradiated at 290 °C in a research reactor. Thermal ageing at 450 °C was also carried out to compare with the results in the neutron irradiation. The addition of Mn resulted in larger hardening and higher cluster number density in both thermal ageing and neutron irradiation. In FeCu0.8NiMn alloy, the size distribution of Cu-enriched clusters formed in 62-h thermal ageing (almost peak hardening) was very similar to that formed in the neutron irradiation, indicating they are on a similar growing stage. But the average Ni and Mn composition in clusters formed in neutron irradiation was higher. A good linear relationship between hardening and the square root of cluster volume fraction for both neutron irradiation and thermal ageing data was found.