Bandgap engineering of novel peryleno[1, 12-bcd]thiophene sulfone-based conjugated co-polymers for significantly enhanced hydrogen evolution without co-catalyst. Issue 38 (25th September 2020)

• Record Type: Journal Article
• Authors: Ye, Haonan; Wang, Zhiqiang; Yang, Zhicheng; Zhang, Shicong; Gong, Xueqing; Hua, Jianli
• Is Part Of: Journal of materials chemistry. Volume 8:Issue 38(2020)
• Page Start: 20062
• Page End: 20071
• Publication Date: 2020-09-25
• Subjects: Materials -- Research -- Periodicals; Chemistry, Analytic -- Periodicals; Environmental sciences -- Research -- Periodicals; 543.0284
• DOI: 10.1039/d0ta07286a
• Languages: English
• ISSNs: 2050-7488

Abstract

Abstract : A peryleno[1, 12- bcd ]thiophene sulfone based conjugated co-polymer PS-5 achieved so far highest HERs of 7.5 mmol h −1 g −1 without Pt-loading. Abstract : Low-cost conjugated polymers as efficient photocatalytic semiconductors for hydrogen evolution have attracted worldwide attention in recent years. However, the narrow visible-light absorption spectrum, fast electron–hole recombination and expensive co-catalysts have limited their large-scale practical application in water splitting. In this work, we first developed the new peryleno[1, 12- bcd ]thiophene sulfone unit with extended π-conjugation, then prepared a series of sulfone-based hybrid conjugated co-polymers (PS-1–PS-8 ) by statistically adjusting the molar ratio of the monomer. The experimental results and DFT calculations indicated that with the gradual increase in the peryleno[1, 12- bcd ]thiophene sulfone contents in the polymer backbone, the optical bandgaps of co-polymers could be fine-tuned from 2.72 eV to 1.58 eV, and showed a red-shift in the visible-light region for improving the light-capturing capability. Besides, the internal charge separation capability along the co-polymers (PS-1–PS-8 ) was promoted. However, the driving force for proton reduction and the dispersibility of these co-polymers in aqueous solution were gradually decreased. When the molar ratio of dibenzo[ b, d ]thiophene sulfone to peryleno[1, 12- bcd ]thiophene sulfone was 19 : 1, the polymer PS-5 achieved the highest hydrogen evolution rate (HER), so far, of 7.5 mmol h −1 g −1 without co-catalyst under visible light, with an apparent quantum yield (AQY) of 15.3% at 420 nm. The HER performance was almost 3 times higher than that of the typical dibenzo[ b, d ]thiophene sulfone-based conjugated polymer P7 . This work provides a strategy for maximizing the HERs of organic semiconductors by balancing the bandgap, charge recombination, driving force and wettability.