Production of Fe nanoparticles from γ-Fe2O3 by high-pressure hydrogen reduction. Issue 10 (2nd September 2020)

• Record Type: Journal Article
• Authors: Dirba, I.; Schwöbel, C. A.; Zintler, A.; Komissinskiy, P.; Molina-Luna, L.; Gutfleisch, O.
• Is Part Of: Nanoscale advances. Volume 2:Issue 10(2020)
• Page Start: 4777
• Page End: 4784
• Publication Date: 2020-09-02
• Subjects: 620.5
• DOI: 10.1039/d0na00635a
• Languages: English
• ISSNs: 2516-0230

Abstract

Abstract : In this work, the reduction of iron oxide γ-Fe2 O3 nanoparticles by hydrogen at high pressures is studied. Abstract : In this work, the reduction of iron oxide γ-Fe2 O3 nanoparticles by hydrogen at high pressures is studied. Increasing the hydrogen pressure enables reduction of γ-Fe2 O3 to α-Fe at significantly lower temperatures. At low pressures, a temperature of 390 °C is necessary whereas at 530 bar complete reduction can be realized at temperatures as low as 210 °C. This leads to significant improvement in the final particle morphology, maintaining high surface-to-volume ratio of the nanoparticles with an average size of 47 ± 5 nm which is close to that of the precursor γ-Fe2 O3 . Neck formation, coalescence and growth during reduction can be significantly suppressed. Investigations of magnetic properties show that saturation magnetization of the reduced α-Fe nanoparticles decreases with particle size from 209 A m 2 kg −1 at 390 °C reduction temperature to 204 A m 2 kg −1 at 210 °C. Coercivity for the fine iron particles reaches 0.076 T which exceeds the theoretical anisotropy field. This is attributed to nano-scale surface effects.