Transformation of the reabsorption characteristics of lignite treated by low and high temperature drying process. Issue 14 (1st October 2020)

• Record Type: Journal Article
• Authors: Wu, Yuanmo; Zhang, Shouyu; Li, You; Li, Hao; Song, Xiaobing
• Is Part Of: Drying technology. Volume 38:Issue 14(2020)
• Page Start: 1857
• Page End: 1868
• Publication Date: 2020-10-01
• Subjects: Lignite -- drying -- effective water-filled porosity -- oxygen-containing functional groups -- reabsorption; Drying -- Periodicals; Desiccation; 660.28426
• DOI: 10.1080/07373937.2019.1680560
• Languages: English
• ISSNs: 0737-3937

Abstract

Abstract: The reabsorption characteristics of the lignite treated by low and high temperature drying process were addressed in the paper. The information about the moisture form, functional groups, effective water-filled porosities and equilibrium moisture content of the lignite before and after the drying process was investigated using Differential scanning calorimetry (DSC), Fourier transform infrared (FTIR) spectroscopy, nuclear magnetic resonance (NMR) spectroscopy and a self-made reabsorption device, respectively. The results show that the low drying temperature (140, 190, 230 °C, 10 min, N2 ) has little impact on the effective water-filled porosities of the resulted samples, whereas it has a great influence on the main oxygen-containing functional groups, which amount firstly decreases and then increases with the drying temperature increasing. In the case of the lignite samples dried under high-temperature (600, 700, 800 °C, 30 s, N2 ), the amount of the effective water-filled porosity of the sample decreases and the amount of oxygen-containing functional groups increases as the temperature increasing. The reabsorption capability of the high temperature dried sample is much lower than that of the sample treated under low drying temperature. The reabsorption characteristics of the low-temperature dried samples are affected by the amount of the oxygen-containing functional groups, while the effective water-filled porosity is main factor for the lignite samples derived from high temperature drying process. Moreover, the work gives a good evidence that the high-temperature drying process is an effective choose for lignite upgrading.