Bifunctional catalytic activity of Zn1−xFexO toward the OER/ORR: seeking an optimal stoichiometry. Issue 38 (28th September 2020)

• Record Type: Journal Article
• Authors: Rajić, Vladimir; Stojković Simatović, Ivana; Veselinović, Ljiljana; Čavor, Jelena Belošević; Novaković, Mirjana; Popović, Maja; Škapin, Srečo Davor; Mojović, Miloš; Stojadinović, Stevan; Rac, Vladislav; Častvan, Ivona Janković; Marković, Smilja
• Is Part Of: Physical chemistry chemical physics. Volume 22:Issue 38(2020)
• Page Start: 22078
• Page End: 22095
• Publication Date: 2020-09-28
• Subjects: Chemistry, Physical and theoretical -- Periodicals; 541.3
• DOI: 10.1039/d0cp03377d
• Languages: English
• ISSNs: 1463-9076

Abstract

Abstract : Eco-friendly and rapid microwave processing of a precipitate was used to produce Fe-doped zinc oxide (Zn1− x Fe x O, x = 0, 0.05, 0.1, 0.15 and 0.20) nanoparticles, which were tested as catalysts toward the ORR and OER in a moderately alkaline solution. Abstract : Eco-friendly and rapid microwave processing of a precipitate was used to produce Fe-doped zinc oxide (Zn1− x Fe x O, x = 0, 0.05, 0.1, 0.15 and 0.20; ZnO:Fe) nanoparticles, which were tested as catalysts toward the oxygen reduction reaction (ORR) and oxygen evolution reaction (OER) in a moderately alkaline solution. The phase composition, crystal structure, morphology, textural properties, surface chemistry, optical properties and band structure were examined to comprehend the influence of Zn 2+ partial substitution with Fe 3+ on the catalytic activity of ZnO:Fe. Linear sweep voltammetry showed an improved catalytic activity of ZnO:5Fe toward the ORR, compared to pure ZnO, while with increased amounts of the Fe-dopant the activity decreased. The improvement was suggested by a more positive onset potential (0.394 V vs. RHE), current density (0.231 mA cm −2 at 0.150 V vs. RHE), and faster kinetics (Tafel slope, b = 248 mV dec −1 ), and it may be due to the synergistic effect of (1) a sufficient amount of surface oxygen vacancies, and (2) a certain amount of plate-like particles composed of crystallites with well developed (0001) and (0001̄) facets. Quite the contrary, the OER study showed that the introduction of Fe 3+ ions into the ZnO crystal structure resulted in enhanced catalytic activity of all ZnO:Fe samples, compared to pure ZnO, probably due to the modified binding energy and an optimized band structure. With the maximal current density of 1.066 mA cm −2 at 2.216 V vs. RHE, an onset potential of 1.856 V vs. RHE, and the smallest potential difference between the OER and ORR (Δ E = 1.58 V), ZnO:10Fe may be considered a promising bifunctional catalyst toward the OER/ORR in moderately alkaline solution. This study demonstrates that the electrocatalytic activity of ZnO:Fe strongly depends on the defect chemistry and consequently the band structure. Along with providing fundamental insight into the electrocatalytic activity of ZnO:Fe, the study also indicates an optimal stoichiometry for enhanced bifunctional activity toward the OER/ORR, compared to pure ZnO.