Characterization of a Bioresorbable Magnesium-Reinforced PLA-Integrated GTR/GBR Membrane as Dental Applications. (19th September 2020)

• Record Type: Journal Article
• Authors: Du, Xin; Song, Yahui; Xuan, Xinxin; Chen, Shuzhen; Wu, Xia; Jiang, Heng Bo; Lee, Eui-Seok; Wang, Xiaohui
• Other Names: Zhao Ying Guest Editor.
• Is Part Of: Scanning. Volume 2020(2020)
• Publication Date: 2020-09-19
• Subjects: Scanning electron microscopy -- Periodicals; 502.825
• DOI: 10.1155/2020/6743195
• Languages: English
• ISSNs: 0161-0457

Abstract

Abstract : Inferior mechanical properties have always been a limitation of the bioresorbable membranes in GBR/GTR. This study is aimed at fabricating a bioresorbable magnesium-reinforced polylactic acid- (PLA-) integrated membrane and investigating its mechanical properties, degradation rate, and biocompatibility. The uncoated and fluoride-coated magnesium alloys, AZ91, were made into strips. Then, magnesium-reinforced PLA-integrated membrane was made through integration. PLA strips were used in the control group instead of magnesium strips. Specimens were cut into rectangular shape and immersed in Hank's Balanced Salt Solution (HBSS) at 37°C for 4, 8, and 12 d. The weight loss of the AZ91 strips was measured. Three-point bending tests were conducted before and after the immersion to determine the maximum load on specimens. Potentiodynamic polarization (PDP), electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM), and energy-dispersive spectroscopy (EDS) were conducted on coated and uncoated AZ91 plates to examine corrosion resistance. Murine fibroblast and osteoblast cells were cultured on circular specimens and titanium disks for 1, 3, and 5 d. Thereafter, WST test was performed to examine cell proliferation. As a result, the coated and uncoated groups showed higher maximum loads than the control group at all time points. The weight loss of AZ91 strips used in the coated group was lower than that in the uncoated group. PDP, EIS, SEM, and EDS showed that the coated AZ91 had a better corrosion resistance than the uncoated AZ91. The cell proliferation test showed that the addition of AZ91 did not have an adverse effect on osteoblast cells. Conclusively, the magnesium-reinforced PLA-integrated membrane has excellent load capacity, corrosion resistance, cell affinity, and proper degradation rate. Moreover, it has great potential as a bioresorbable membrane in the GBR/GTR application.