Sulphide stress cracking of a valve stem of duplex stainless steel. (December 2018)

• Record Type: Journal Article
• Authors: Chandra, K.; Singh, A.P.; Kain, Vivekanand; Kumar, Niraj
• Is Part Of: Engineering failure analysis. Volume 94(2018)
• Page Start: 41
• Page End: 46
• Publication Date: 2018-12
• Subjects: Failure analysis -- Cracks -- Corrosion -- Hydrogen embrittlement -- Microstructures; System failures (Engineering) -- Periodicals; Fracture mechanics -- Periodicals; Reliability (Engineering) -- Periodicals; Pannes -- Périodiques; Rupture, Mécanique de la -- Périodiques; Fiabilité -- Périodiques; Fracture mechanics; Reliability (Engineering); System failures (Engineering); Periodicals; Electronic journals; 620.112
• DOI: 10.1016/j.engfailanal.2018.07.033
• Languages: English
• ISSNs: 1350-6307

Abstract

Abstract: The present paper describes a failure investigation of a double disc valve stem made of duplex stainless steel 329 (UNS S32900). The valve stem which operated in moist H2 S environment at 128 °C in a heavy water plant had undergone cracking during operation. The microstructure of the stem material showed precipitates of σ-phase at ferrite/austenite boundaries and elongated oxide inclusions. The formation of σ-phase had occurred during the manufacturing stage of the stem. The crack propagation was more favourable in the ferrite phase and along the ferrite/austenite boundaries where precipitates of σ-phase were formed. It was concluded that the valve stem failed by sulphide stress cracking due to hydrogen embrittlement of ferrite phase. Recommendations to avoid such failures are also suggested. Highlights: An investigation of cracking of a valve stem of duplex stainless steel is described. The stem operated in moist H2 S environment at 128 °C in a heavy water plant. Stem material contained σ-phase which had formed during the manufacturing stage. Crack propagation was more favourable in ferrite and where σ-phase was present. Stem failed by sulphide stress cracking due to hydrogen embrittlement of ferrite.