Hydrogen sorption by Ni-coated titanium alloy VT1-0. (13th April 2017)

• Record Type: Journal Article
• Authors: Kudiiarov, V.N.; Kashkarov, E.B.; Syrtanov, M.S.; Lider, A.M.
• Is Part Of: International journal of hydrogen energy. Volume 42:Number 15(2017)
• Page Start: 10604
• Page End: 10610
• Publication Date: 2017-04-13
• Subjects: Hydrogen -- Titanium -- Nickel -- Magnetron sputtering -- XRD -- Titanium powder; Hydrogen as fuel -- Periodicals; Hydrogène (Combustible) -- Périodiques; Hydrogen as fuel; Periodicals; 665.81
• DOI: 10.1016/j.ijhydene.2017.02.036
• Languages: English
• ISSNs: 0360-3199

Abstract

Abstract: Sorption properties of titanium alloy VT1-0 coated by nickel layer using dc magnetron sputtering were investigated in this paper. The crystalline structure of the coating as well as evaluation of its thickness was analyzed by X-ray diffraction in grazing incidence geometry. It was revealed that the nickel coating significantly increases the hydrogen sorption rate of titanium alloy compared to pure titanium covered with its original oxide layer. Hydrogen sorption rate reduces approximately from 10 −3 to 10 −4 wt.%/s with increasing the nickel thickness from 1 to 2.6 μm, respectively. Hydrogen sorption kinetics strongly depends on the hydrogenation parameters. The increase of both temperature in the range of 350–550 °C and hydrogen pressure from 1 to 2 atm leads to increase of hydrogen sorption rate. Highlights: The thin Ni layers were deposited by dcMS to improve hydrogen sorption rate of titanium alloy VT1-0. A linear dependence between Ni coating thickness and deposition time is observed. The gradual decrease of the hydrogen sorption rate with increasing Ni coating thickness is observed. Higher temperature and hydrogen pressure increase hydrogen sorption rate.