Experimental analysis and mechanical characterization of Al 6061/alumina/bagasse ash hybrid reinforced metal matrix composite using vacuum-assisted stir casting method. (November 2020)

• Record Type: Journal Article
• Authors: Chandla, Nagender Kumar; Yashpal, ; Kant, Suman; Goud, MM; Jawalkar, CS
• Is Part Of: Journal of composite materials. Volume 54:Number 27(2020)
• Page Start: 4283
• Page End: 4297
• Publication Date: 2020-11
• Subjects: Al 6061 -- alumina -- bagasse ash -- hybrid-reinforced metal matrix composite -- single-reinforced metal matrix composite -- stir casting; Composite materials -- Periodicals; Composites -- Périodiques; 620.118
• DOI: 10.1177/0021998320929417
• Languages: English
• ISSNs: 0021-9983

Abstract

This experimental analysis aimed to fabricate low cost, lightweight metal matrix composite using Al 6061 as matrix material and alumina (Al2 O3 ) and bagasse ash as reinforcing material through stir casting process. In this process one cast of single reinforced composite (Al 6061/5 wt% Al2 O3 ) and three casts of hybrid reinforced composite (Al 6061/5 wt% Al2 O3 / 4, 6, 8 wt% bagasse ash) were developed and processed as per ASTM standards followed by mechanical (micro-hardness, ductility, compression, tensile, and impact strength), physical (density and porosity), and microstructure (optical and SEM microscopy) characterization. The mechanical properties such as tensile strength, hardness, and compressive strength showed good improvements in the manufactured hybrid reinforced metal matrix composite (HRMMC) in comparison with the single reinforced metal matrix composite (SRMMC). The tensile strength and hardness of developed composite increased continuously with an increase in bagasse ash contents up to 6 wt% having maximum increment of 9.09% (tensile) and 16.5% (hardness) and thereafter both decreased for 8 wt% of bagasse ash, respectively. The results of impact strength and ductility of Al 6061/Al2 O3 /bagasse ash showed marginal reduction, as the wt% of reinforcements increased. It was found that the density of HRMMC was less than the SRMMC and it decreased with increasing wt% of reinforcements however, the composite contained some porosity percentage (max. value 2.26%), which increased as the wt% of reinforcement increased. The microstructure analysis showed fair distribution with good interface bonding up to 6 wt% bagasse ash.