A study on the acidity of sulfated CuO layers grown by surface reconstruction of Cu2O with specific exposed facets. Issue 12 (28th May 2020)

• Record Type: Journal Article
• Authors: Wu, Yanan; Chen, Xin; Huang, Daofeng; Zhang, Li; Ren, Yuanhang; Tang, Gangfeng; Chen, Xueying; Yue, Bin; He, Heyong
• Is Part Of: Catalysis science & technology. Volume 10:Issue 12(2020)
• Page Start: 3985
• Page End: 3993
• Publication Date: 2020-05-28
• Subjects: Catalysis -- Periodicals; 541.395
• DOI: 10.1039/d0cy00892c
• Languages: English
• ISSNs: 2044-4753

Abstract

Abstract : Surface reconstruction and sulfation improve the acidity of Cu2 O, and moderate Lewis acid sites are the active sites in Pechmann condensation. Abstract : Three cuprous oxide samples with exposed {111}, {100}/{111} and {100} facets were synthesized and then oxidized in air by calcination to form surface reconstructed Cu2 O@CuO samples. 31 P MAS NMR with trimethylphosphine as the probe molecule was applied to characterize the surface acidity of the samples. It was found that the Cu2 O@CuO samples exhibit higher Lewis acid density compared with pristine Cu2 O samples. After sulfation, the SO4 2− /Cu2 O@CuO samples have similar total acid density, which is much higher than that of Cu2 O@CuO samples. Moreover, three types of Lewis acid sites assigned to unsaturated 2-coordinated Cu sites, unsaturated 2-coordinated Cu sites bonded to SO4 2− and unsaturated 3-coordinated Cu sites were observed on SO4 2− /Cu2 O@CuO. The density of these three Lewis acid sites varies from different samples. In the Pechmann condensation reaction, it was observed that strong Lewis acid sites are deactivated due to adsorption of the reactants while moderate Lewis acid sites act as the actual active sites.