Pulsed-flow growth of polar, semipolar and nonpolar AlGaN. Issue 25 (8th June 2020)

• Record Type: Journal Article
• Authors: Dinh, Duc V.; Hu, Nan; Honda, Yoshio; Amano, Hiroshi; Pristovsek, Markus
• Is Part Of: Journal of materials chemistry. Volume 8:Issue 25(2020)
• Page Start: 8668
• Page End: 8675
• Publication Date: 2020-06-08
• Subjects: Materials -- Periodicals; Chemistry, Analytic -- Periodicals; Optical materials -- Research -- Periodicals; Electronics -- Materials -- Research -- Periodicals; 543.0284
• DOI: 10.1039/d0tc01369b
• Languages: English
• ISSNs: 2050-7526

Abstract

Abstract : The impacts of pulsed-flow growth on aluminium incorporation in polar (0001), semipolar (101̄3) and (112̄2), as well as nonpolar (101̄0) AlGaN layers have been investigated. Abstract : The impacts of pulsed-flow growth on aluminium incorporation in polar (0001), semipolar (101̄3) and (112̄2), as well as nonpolar (101̄0) AlGaN layers have been investigated. The layers were grown simultaneously on differently oriented AlN/sapphire templates by metal–organic vapour phase epitaxy. The AlN mole fraction (0 < x AlN ≤ 0.85) of the layers was varied by simply changing the supply time of the aluminium precursor while keeping nitrogen and gallium precursors constant. Phase separation has been observed for the (0001) and (112̄2) layers by X-ray diffraction, and is attributed to their different surface reconstructions during growth. In contrast, no phase separation has been observed for the (101̄0) and (101̄3) layers, attributed to their stable surfaces during growth. The AlN mole fraction of the differently oriented layers generally follows the order: (112̄2) < (0001) < (101̄3) ≤ (101̄0), attributed to their different surface dangling-bond densities. By means of room-temperature photoluminescence measurements, high carbon-incorporation has quantitatively been found in all the layers.