Pulsed current-assisted joining of copper to graphite using Ti-Cu brazing layers. (2020)

• Record Type: Journal Article
• Authors: Vidyuk, T.M.; Dudina, D.V.; Esikov, M.A.; Mali, V.I.; Anisimov, A.G.; Bokhonov, B.B.; Batraev, I.S.
• Is Part Of: Materials today. Volume 25:Part 3(2020)
• Page Start: 377
• Page End: 380
• Publication Date: 2020
• Subjects: Brazing -- Copper -- Graphite -- Ti-Cu alloy -- Spark plasma sintering -- Titanium carbide -- Microstructure; Materials science -- Congresses -- Periodicals; 620.1
• DOI: 10.1016/j.matpr.2019.12.095
• Languages: English
• ISSNs: 2214-7853

Abstract

Abstract: Copper-graphite joints are functional elements of many electronic and electromechanical devices. Unique properties of graphite, such as the ability to withstand high temperatures, a low friction coefficient and high thermal and electrical conductivities make it an attractive material for various applications. For enabling efficient heat sink or making sliding electrical contacts, graphite requires joining to metallic copper. Poor wettability between copper and graphite is a problem that needs to be overcome to form a reliable joint. In the present work, we used a Ti25 Cu75 alloy to braze graphite to copper in a pulsed current-assisted process. Brazing was carried out in a Spark Plasma Sintering (SPS) apparatus under a uniaxial pressure of 13 MPa. The SPS conditions – a possibility of localized heating under an applied pressure in dynamic vacuum – are beneficial for the joining processes of conductive materials. For joining graphite and copper plates, a die-free configuration was used. The microstructure and the phase composition of the copper-graphite brazed joints were investigated. Strong joints were formed when the upper electrode temperature measured by a thermocouple reached 700 °C. At the graphite-alloy interface, a TiC layer 0.5–1 μm thick was formed; in addition, TiC particles were found in the metallic matrix in a layer 5–10 μm thick adjacent to the graphite plate. The tensile strength of the brazed joint was higher than the tensile strength of graphite (13 MPa).