Preparation of near net size porous alumina‐calcium aluminate ceramics by gelcasting‐pore‐forming agent processs. Issue 8 (7th March 2020)

• Record Type: Journal Article
• Authors: Hao, Bian‐Lei; Lang, Ying; Bian, Da‐Qian; Wang, Chang‐An
• Is Part Of: Journal of the American Ceramic Society. Volume 103:Issue 8(2020)
• Page Start: 4602
• Page End: 4610
• Publication Date: 2020-03-07
• Subjects: alumina -- calcium aluminate -- near net size preparation -- porous ceramics -- shrinkage; Ceramics -- Periodicals; 620.1405
• DOI: 10.1111/jace.17075
• Languages: English
• ISSNs: 0002-7820

Abstract

Abstract: In the processing of porous ceramics, shrinkage from green body to sintered compact during drying and sintering is one of the key concerns which affect microstructure and properties of porous ceramics. Through releasing gases from the burning of the pore forming agents, and volume expansion from the formation of low density resultants during sintering, the sintering shrinkage can be effectively compensated and near net size preparation can be achieved. Herein, near net size porous alumina‐calcium aluminate ceramics with controllable shrinkage have been prepared using a combination of gelcasting and pore‐forming agent process by adjusting the amount of CaCO3 and polymethyl methacrylate (PMMA) microspheres added. Al2 O3 and CaCO3 were used as raw materials, PMMA microspheres were used as pore‐forming agent, isobutylene/maleic anhydride copolymer (Isobam104) was used as gelling agent and dispersing agent. The effects of the addition amounts of CaCO3 and PMMA in the slurry on the phase composition, shrinkage, porosity, and strength of porous alumina‐calcium aluminate ceramics were investigated. The results show that as the CaCO3 addition amount increases from 0 to 20 wt%, the shrinkage of the samples gradually decreases from 7.3% to −1.4%, and the consequent porosity increases from 58% to 66%, while the compressive strength increases from 5.9 to 15.5 MPa. When PMMA content increases from 10 to 50 wt%, the shrinkage of the samples decreases first and then increases, the porosity increases from 51% to 74%, and the compressive strength decreases from 12.5 to 5.3 MPa. The mechanisms for controlling shrinkages during preparation of porous alumina‐calcium aluminate ceramics can be attributed to the following aspects: on one hand, gas release from burning of PMMA and decomposition of CaCO3 during sintering; on the other hand, volume expansion due to the formation of lower density calcium aluminates which come from the reactions between CaO and Al2 O3 . The near net size preparation technique is of great significance for the manufacture of porous ceramics since the subsequent machining cost can be effectively reduced.