Chemical looping gasification of cotton stalk with bimetallic Cu/Ni/olivine as oxygen carrier. (27th April 2020) - Pan, Yue
Summary: Bimetallic Cu/Ni/olivine oxygen carriers (OCs) were prepared using olivine as support material for chemical looping gasification (CLG). The cyclic redox behaviors and oxygen carrying capacity (Ro ) of OCs were evaluated by thermo‐gravimetric analysis. The effect of Cu/Ni ratio, gasification temperature, steam to biomass ratio (S/B), oxygen carrier to biomass ratio (OC/B) on CLG of cotton stalk has been studied in a fixed bed. The OCs characterized using BET surface area, scanning electron microscopy (SEM), X‐ray diffraction (XRD), temperature‐programmed reduction (TPR) to investigate the physicochemical property of OCs during CLG. Result shows that the sintering problem of OC was progressively alleviated with the increasing Cu/Ni ratio. The olivine behaves as suitable OC support with oxygen carrying capacity of 1.07%. The redox reactivity of all of the OCs kept well during multiple redox cycles. The Ro of OCs progressively increased with the Cu/Ni ratio. By comparing the product gas concentration, carbon conversion, H2 + CO yield and gas yield over the invested OCs, the Cu9/Ni6/O was found to demonstrate better comprehensive CLG performance due to the synergistic effect of Cu and Ni. The maximum gas yield, H2 + CO yield and carbon conversion with Cu9/Ni6/O can be obtained at the S/B of 0.8 and OC/B of 2. Compared to theoretical value, 65% of lattice oxygen has been supplied by Cu9/Ni6/O during actual CLG process. The OC displayed better reactivity due to basic crystalline phase being preserved well during multiple CLG cycles. Abstract : The bimetallic Cu/Ni/olivine as oxygen carrier (OC) was used for chemical looping gasification (CLG) of cotton stalk. The cyclic redox behaviors of OC were evaluated by thermo‐gravimetric analysis. Synergetic effect of Ni and Cu promoted chemical looping gasification of biomass. Cu/Ni/olivine preserved stable performance during multiple CLG cycles.