Thermal properties of sodium borosilicate glasses as a function of sulfur content. Issue 6 (27th February 2020)

• Record Type: Journal Article
• Authors: Lonergan, Jason M.; Lonergan, Charmayne; Silverstein, Joshua; Cholsaipant, Pornsinee; McCloy, John
• Is Part Of: Journal of the American Ceramic Society. Volume 103:Issue 6(2020)
• Page Start: 3610
• Page End: 3619
• Publication Date: 2020-02-27
• Subjects: borosilicate glass -- nuclear waste -- thermal properties; Ceramics -- Periodicals; 620.1405
• DOI: 10.1111/jace.17057
• Languages: English
• ISSNs: 0002-7820

Abstract

Abstract: Sulfur trioxide (SO3 ) additions, up to 3.0 mass%, were systematically investigated for effects on the physical properties of sodium borosilicate glass melted in air, with a sulfur‐free composition of 50SiO2 –10Al2 O3 –12B2 O3 –21Na2 O–7CaO (mass%). Solubility measurements, using electron microscopy chemical analysis, determined the maximum loading to be ~1.2 mass% SO3 . It was found that measured sulfur (here as sulfate) additions up to 1.18 mass% increased the glass transition temperature by 3%, thermal diffusivity by 11%, heat capacity by 10%, and thermal conductivity by 20%, and decreased the mass density by 1%. Structural analysis, performed with Raman spectroscopy, indicated that the borosilicate network polymerized with sulfur additions up to 3.0 mass%, presumably due to Na2 O being required to charge compensate the ionic SO 4 2 - additions, thus becoming unavailable to form non‐bridging oxygen in the silicate network. It is postulated that this increased cross‐linking of the borosilicate backbone led to a structure with higher dimensionality and average bond energy. This increased the mean free paths and vibration frequency of the phonons, which resulted in the observed increase in thermal properties.