Evolution behaviour of nonmetallic inclusions in Ti-bearing 11Cr stainless steel with calcium treatment. (2nd January 2020) - Li, Jingyu
ABSTRACT: Nonmetallic inclusions formed during the Ti-stabilized stainless steelmaking process can induce the clogging in the submerged entry nozzle during continuous casting. To investigate the formation mechanism of nonmetallic inclusions in Ti-stabilized stainless steel, steel specimens were taken at different stages in industrial trials. The characteristics of inclusions and the chemical compositions of steel were analysed. After 10 min of Al deoxidation, the main type of inclusions in samples was irregular MgO·Al2 O3 . With titanium addition after calcium treatment, the irregular dual phase CaO–TiO x –Al2 O3 –MgO inclusions were formed. The steel compositions of most samples were located in or close to the Al2 O3 –TiO x liquid oxide phase field. According to experiment and thermodynamic results, the solid CaTiO3 and/or CaO·2Al2 O3 inclusions were formed during titanium addition when the molten steel contained more than 20 ppm calcium. The effect of the initial calcium content on the formation of Ca–Al–Ti–O inclusions during titanium addition was discussed.