Preparation and cyclic oxidation behaviour of Re doped aluminide coatings on a Ni-based single crystal superalloy. (March 2020)

• Record Type: Journal Article
• Authors: Li, W.; Sun, J.; Liu, S.B.; Liu, Y.D.; Fu, L.B.; Wang, T.G.; Jiang, S.M.; Gong, J.; Sun, C.
• Is Part Of: Corrosion science. Volume 164(2020)
• Publication Date: 2020-03
• Subjects: Rhenium -- Metal coatings -- Superalloys -- SEM -- Oxidation; Corrosion and anti-corrosives -- Periodicals; 620.11223
• DOI: 10.1016/j.corsci.2019.108354
• Languages: English
• ISSNs: 0010-938X

Abstract

Highlights: Re doped aluminide coatings were prepared by electroplating and arc ion plating. Adding appropriate amount of Re decreased the oxidation rate of the coating. The phase transition of θ to α-Al2 O3 could be accelerated by Re doping. Re-contained IDZ had the effect of diffusion barrier. Electroplating Ni improved the oxidation resistance of the coating. Abstract: Three Re doped aluminide coatings with different Re content were prepared by electroplating and subsequent arc ion plating (AIP) method. Cyclic oxidation behaviour of all coatings was carried out at 1100 ℃. The results indicated that the oxidation resistance was significantly improved with an appropriate amount of Re addition and electroplating Ni. Besides, Re accelerated the θ-to-α Al2 O3 phase transformation. The oxidation mechanisms of aluminide coatings with Re doped and Ni electroplated were discussed as well.