Non-hardening embrittlement mechanism of pressure vessel steel Ni-Cr-Mo-V welds during thermal aging. (February 2020)

• Record Type: Journal Article
• Authors: Wei, Guojun; Wang, Chenglong; Yang, Xingwang; Tong, Zhenfeng; Wu, Wenwang
• Is Part Of: Advances in mechanical engineering. Volume 12:Number 2(2020)
• Publication Date: 2020-02
• Subjects: Reactor pressure vessel -- Charpy impact test -- Ni-Cr-Mo-V steel weld -- segregation of impurity -- non-hardening embrittlement; Mechanical engineering -- Periodicals; 621.05
• DOI: 10.1177/1687814020904567
• Languages: English
• ISSNs: 1687-8132

Abstract

The mechanical performance of reactor pressure vessel materials is an important factor in the safety and economics of the operation of a nuclear power plant. The ductile-to-brittle transition temperature tested by Charpy impact test is the key parameter for evaluating the reactor pressure vessel embrittlement. In this article, the study of thermal aging embrittlement of temperature sets of reactor pressure vessel surveillance Ni-Cr-Mo-V steel weld metal was conducted by Charpy impact test. The thermal aging effect on the impact fracture behavior was analyzed. The impact test of the three batches of weld surveillance sample indicated that the weld metal embrittled during thermal aging. The study of impact fracture and Auger electron spectroscopy indicated that the element P segregated to the grain boundaries and lowered their cohesion strength during the long-term thermal aging. Therefore, the non-hardening embrittlement of Ni-Cr-Mo-V steel welds in a reactor pressure vessel caused by segregation of impurity elements P occurs during thermal aging.