Room-temperature synthesized porous Cu(OH)2/Cu7S4 hybrid nanowires as a high-performance electrode material for asymmetric supercapacitors. Issue 2 (13th December 2019)

• Record Type: Journal Article
• Authors: Sun, Mengxuan; Li, Zhijie; Fang, Qisheng; Han, Shaobo; Cai, Chao; Li, Hao; Shen, Wenzhong; Liu, Xiaoteng; Fu, YongQing
• Is Part Of: Journal of materials chemistry. Volume 8:Issue 2(2020)
• Page Start: 724
• Page End: 734
• Publication Date: 2019-12-13
• Subjects: Materials -- Research -- Periodicals; Chemistry, Analytic -- Periodicals; Environmental sciences -- Research -- Periodicals; 543.0284
• DOI: 10.1039/c9ta11515c
• Languages: English
• ISSNs: 2050-7488

Abstract

Abstract : Porous Cu(OH)2 /Cu7 S4 hybrid nanowires were efficiently prepared from the [Cu(tu)]Cl·1/2H2 O (tu = thiourea) precursor in the solution of 2 M KOH and showed large capacity. Abstract : Copper-based nanomaterials have attracted significant interest as electrode materials for supercapacitors due to their low cost and environmental friendliness, however, their low capacitances inhibit their commercial applications. Design and application of porous and hybrid 1-D nanostructures as electrode materials is an effective approach to improve their capacitance. In this work, porous Cu(OH)2 /Cu7 S4 hybrid nanowires were synthesized at room temperature using a self-sacrificial template method. They had large surface areas and pore volumes, which provided numerous active sites for faradaic reactions and facilitated fast ion diffusion and electron transport during the charge–discharge process. Cu(OH)2 /Cu7 S4 nanowires coated on nickel foam were used as electrodes without using any conductive agent or binder. Results showed that a high specific capacity of 1610.8 C g −1 was achieved at a current density of 4 A g −1, and a large value of 765.0 C g −1 was still retained at a higher current density of 30 A g −1 . An asymmetric supercapacitor assembled using this Cu(OH)2 /Cu7 S4 positive electrode and an active carbon negative electrode demonstrated a high energy density of 48.1 W h kg −1 at a power density of 429.3 W kg −1 and a good cycling stability, suggesting that these porous Cu(OH)2 /Cu7 S4 hybrid nanowires are promising electrode materials for supercapacitors.