Polycrystalline scintillators for large area detectors in HEP experiments. (30th June 2017)

• Record Type: Journal Article
• Authors: Dosovitskiy, G.; Fedorov, A.; Karpyuk, P.; Kuznetsova, D.; Mikhlin, A.; Kozlov, D.; Dosovitskiy, A.; Korjik, M.
• Is Part Of: Journal of instrumentation. Volume 12:Number 6(2017:Jun.)
• Page Start: C06045
• Page End: C06045
• Publication Date: 2017-06-30
• Subjects: Scintillators and scintillating fibres and light guides -- Detector design and construction technologies and materials -- Radiation-hard detectors -- Calorimeters; Scientific apparatus and instruments -- Periodicals; 502.84
• DOI: 10.1088/1748-0221/12/06/C06045
• Languages: English
• ISSNs: 1748-0221

Abstract

Abstract: After significant increase of the accelerator luminosity throughout the High Luminosity phase of LHC, charged hadrons and neutrons with fluences higher than 10 14 p/cm 2 per year in the largest pseudo-rapidity regions of the detectors will cause increased radiation damage of materials. Increasing activation of the experimental equipment will make periodical maintenance and replacement of detector components difficult. Therefore, the selected materials for new detectors should be tolerant to radiation damage. Y 3 Al 5 O 12 :Ce (YAG:Ce) crystal was found to be one of the most radiation hard scintillation materials. However, production of YAG:Ce in a single crystalline form is costly, because crystal growth is performed at temperature near 1900° C with a very low rate of transformation of a raw material into a crystal. We propose translucent YAG:Ce ceramics as an alternative cheaper solution. Ceramic samples were sintered up to density ∼98% of the theoretical value and were translucent. The samples have demonstrated light yield of 2200 phot./MeV under 662 keV γ -quanta, which gives the expected response to minimum ionizing particle around 3000 phot. for 2 mm thick plate. Scintillation light yield, registered under surface layer excitation with α -particles, was 50–70% higher than for the reference single crystal YAG:Ce.