LuPO4:Yb phosphor with concerted UV and IR thermoluminescent emissions by quantum cutting at high temperatures. Issue 43 (18th July 2019)

• Record Type: Journal Article
• Authors: Zeler, Justyna; Zych, Eugeniusz; Jedoń, Joanna
• Is Part Of: Physical chemistry chemical physics. Volume 21:Issue 43(2019)
• Page Start: 23826
• Page End: 23832
• Publication Date: 2019-07-18
• Subjects: Chemistry, Physical and theoretical -- Periodicals; 541.3
• DOI: 10.1039/c9cp03169c
• Languages: English
• ISSNs: 1463-9076

Abstract

Abstract : Thermoluminescence of LuPO4 :0.1%Yb 3+ sintered ceramics was investigated and simultaneous infrared 2 F5/2 → 2 F7/2 and UV-blue (YbCT 3+ )* → O 2− charge transfer emissions of the Yb 3+ impurity were observed around 150 °C (423 K) for the first time. Abstract : Thermoluminescence of LuPO4 :0.1%Yb 3+ sintered ceramics was investigated and simultaneous infrared 2 F5/2 → 2 F7/2 and UV-blue (YbCT 3+ )* → O 2− charge transfer emissions of the Yb 3+ impurity were observed around 150 °C (423 K) for the first time. Both photons were generated by one excited Yb 3+ *. LuPO4 :Yb 3+ was thus proved to be the first system showing the quantum cutting effect in thermoluminescence. Low concentration of the dopant was proved crucial to observe an intense CT emission at so high temperatures. These data revise deeply those reported previously on the thermal quenching of Yb 3+ charge transfer luminescence in orthophosphates. In was formerly claimed that CT luminescence of Yb 3+ in LuPO4 and similar hosts is quenched below 300 K. Similarly, the thermoluminescent emission of LuPO4 :Yb 3+ above room temperature was previously reported to appear only in the IR part of the spectrum around 980 nm. Our results fundamentally change this picture and prove that CT luminescence of Yb 3+ in orthophosphates appears to be significant even above 150 °C (423 K). We demonstrate the great significance of the activator concentration in its CT luminescence thermal quenching. The Yb 3+ impurity ion was found to act both as an electron trap and as a recombination center. Our data open the possibility to generate intense CT luminescence of Yb 3+ in orthophosphates at room temperature and above which may make such phosphors rational for applications previously considered unattainable for them.