Preparation and characterization of self-crosslinking fluorinated polyacrylate latexes and their pressure sensitive adhesive applications. (December 2019)

• Record Type: Journal Article
• Authors: Fang, Cheng; Zhu, Kai; Zhu, Xinbao; Lin, Zhongxiang
• Is Part Of: International journal of adhesion & adhesives. Volume 95(2019)
• Publication Date: 2019-12
• Subjects: Fluorinated polyacrylate -- Self-crosslinking -- Emulsion polymerization -- Surface property -- Pressure sensitive adhesive; Adhesion -- Periodicals; Adhesives -- Periodicals; Adhésion (Physique) -- Périodiques; Adhésifs -- Périodiques; Adhesie; Kleefstoffen; Adhesion; Adhesives; Periodicals; 668.3
• DOI: 10.1016/j.ijadhadh.2019.102417
• Languages: English
• ISSNs: 0143-7496

Abstract

Abstract: Self-crosslinking fluorinated polyacrylate latexes based on butyl acrylate (BA), fluorine monomer octafluoropentyl methacrylate (OFPMA), self-crosslinking functional monomers acrylic acid (AA) and 2-hydroxyethyl acrylate (HEA) were synthesized by a monomer-starved seeded semi-continuous emulsion polymerization process. The latexes and their corresponding films were characterized by laser particle size analyser, Fourier transform infrared (FTIR) spectroscopy, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), contact angle goniometer, X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM). Results indicated that the particle size of the latexes and the gel content of the films were both independent of the amount of OFPMA employed. On the other hand, the particle size of the latexes decreased and the gel content of the films increased with the incorporation of AA and HEA as expected. Glass transition temperature (Tg ) and the thermal stability of the copolymer were both improved gradually as OFPMA content increased. XPS, AFM and water contact angle measurement indicated that the fluoroalkyl groups had a tendency to enrich on the surface of the films. However, this enrichment of fluorine on the film surface was reduced after the introduction of self-crosslinking functional monomers into the system. Finally, the adhesive property of the latexes was evaluated for application as a pressure sensitive adhesive (PSA).