EIS investigation of a Ce‐based posttreatment step on the corrosion behaviour of Alclad AA2024 anodized in TSA. (7th March 2019) - Prada Ramirez, Oscar Mauricio
Abstract : In the aircraft industry, anodizing and posttreatment steps use Cr (VI) compounds, which, despite offering good corrosion resistance and self‐healing properties, are highly toxic and carcinogenic. Ce compounds are recognized as efficient corrosion inhibitors for Al alloys, and several works report self‐healing ability for these chemicals. In this investigation, the corrosion resistance of Alclad AA2024‐T3 alloy anodized in tartaric‐sulphuric acid (TSA) bath and posttreated in a solution comprising cerium nitrate without and with hydrogen peroxide was evaluated. The purpose is to investigate the potentiality of using hydrothermal treatment in Ce nitrate solution as candidate to replace Cr (VI) posttreatment. The aim is to provide a posttreatment step which, while improving the corrosion resistance, does not plug the mouths of the pores maintaining the adhesion properties of the porous anodic layer. Microstructural characterization was carried out by SEM‐EDS whereas corrosion resistance was evaluated by EIS. The surface analysis showed that the posttreatments, all performed at 50°C, kept the open structure of the pores. EIS analysis showed that the posttreatments performed in the H2 O2 solution for short immersion times were the most effective in improving the corrosion resistance of the samples, whereas electrical equivalent circuit (EEC) fitting of the data indicated sealing of the porous layer during the immersion of the different samples in the test solution. SEM‐EDS analysis of the samples posttreated in the H2 O2 containing solution, prior and after the corrosion test, showed the presence of Ce oxy‐hydroxide randomly deposited on the sample surface, indicating that Ce could be incorporated/stored in the anodic layer.