Comparison of K-doped and pure cold-rolled tungsten sheets: As-rolled condition and recrystallization behaviour after isochronal annealing at different temperatures. (December 2019)
- Record Type:
- Journal Article
- Title:
- Comparison of K-doped and pure cold-rolled tungsten sheets: As-rolled condition and recrystallization behaviour after isochronal annealing at different temperatures. (December 2019)
- Main Title:
- Comparison of K-doped and pure cold-rolled tungsten sheets: As-rolled condition and recrystallization behaviour after isochronal annealing at different temperatures
- Authors:
- Lied, Philipp
Bonnekoh, Carsten
Pantleon, Wolfgang
Stricker, Markus
Hoffmann, Andreas
Reiser, Jens - Abstract:
- Abstract: Severely deformed cold-rolled tungsten is a promising structural material for future fusion reactor applications due to high melting temperature and excellent mechanical properties. However, the fine-grained microstructure after deformation is not stable at temperatures above 800 °C, leading to brittle material behaviour. In this study, we utilize potassium-doping to inhibit recrystallization of tungsten sheets, a mechanism well known from incandescent lamp wires. We produced K-doped tungsten sheets by warm-rolling and subsequent cold-rolling with five different logarithmic strains up to 4.6, and equivalently rolled pure tungsten sheets. Both sets of materials are compared using EBSD and microhardness testing. In both materials, the hardness increases and the grain size along normal direction decreases with strain; the densities of low and high angle boundaries increase in particular during cold-rolling. The K-doped W sheet reaches the highest hardness with 772 ± 8 HV0.1, compared to the pure W sheet with 711 ± 14 HV0.1. All boundaries taken into account, a Hall-Petch relation describes the hardness evolution nicely, except a deviation of the K-doped tungsten sheet rolled to highest strain with its much higher hardness. The similar structural and mechanical properties of both materials in the as-rolled condition allow further studies of recrystallization behaviour of the new K-doped material with a benchmark against the equivalent pure tungsten sheets. IsochronalAbstract: Severely deformed cold-rolled tungsten is a promising structural material for future fusion reactor applications due to high melting temperature and excellent mechanical properties. However, the fine-grained microstructure after deformation is not stable at temperatures above 800 °C, leading to brittle material behaviour. In this study, we utilize potassium-doping to inhibit recrystallization of tungsten sheets, a mechanism well known from incandescent lamp wires. We produced K-doped tungsten sheets by warm-rolling and subsequent cold-rolling with five different logarithmic strains up to 4.6, and equivalently rolled pure tungsten sheets. Both sets of materials are compared using EBSD and microhardness testing. In both materials, the hardness increases and the grain size along normal direction decreases with strain; the densities of low and high angle boundaries increase in particular during cold-rolling. The K-doped W sheet reaches the highest hardness with 772 ± 8 HV0.1, compared to the pure W sheet with 711 ± 14 HV0.1. All boundaries taken into account, a Hall-Petch relation describes the hardness evolution nicely, except a deviation of the K-doped tungsten sheet rolled to highest strain with its much higher hardness. The similar structural and mechanical properties of both materials in the as-rolled condition allow further studies of recrystallization behaviour of the new K-doped material with a benchmark against the equivalent pure tungsten sheets. Isochronal annealing for 1 h was performed at different temperatures between 700 °C and 2200 °C. A sharp decrease in hardness to intermediate values is observed at around 900 °C for both materials, presumably reflecting extended recovery. A second decrease is observed at 1400 °C for pure tungsten, approaching the hardness of a single crystal and indicating recrystallization and severe growth of grains. For K-doped tungsten, however, the occurrence of the second decrease is shifted to higher temperatures from 1400 °C to 1800 °C with increasing strain and an intermediate hardness is maintained up to 1800 °C. We refer this dependence of the recrystallization resistance on strain in the K-doped material to the dispersion of K-bubbles, resulting in increased Zener pinning forces retarding boundary motion. Highlights: Cold-rolling down to 50 μm sheets leads to a very strong texture and high hardness. Small grain size of <180 nm, no saturation in grain size reduction observed. LABs are significantly influencing the hardness following the Hall-Petch relation. Restoration mechanism leads to softening at 900 °C, presumably by extended recovery. K-bubbles inhibit RX at higher temperatures, more effectively with increasing strain. … (more)
- Is Part Of:
- International journal of refractory metals & hard materials. Volume 85(2019)
- Journal:
- International journal of refractory metals & hard materials
- Issue:
- Volume 85(2019)
- Issue Display:
- Volume 85, Issue 2019 (2019)
- Year:
- 2019
- Volume:
- 85
- Issue:
- 2019
- Issue Sort Value:
- 2019-0085-2019-0000
- Page Start:
- Page End:
- Publication Date:
- 2019-12
- Subjects:
- Potassium-doping -- Crystallographic texture -- Grain size distribution -- Hall-Petch relation -- Dislocation interaction -- Recrystallization inhibition
Heat resistant alloys -- Periodicals
Refractory materials -- Periodicals
Metallography -- Periodicals
Alliages réfractaires -- Périodiques
Matériaux réfractaires -- Périodiques
Métallographie -- Périodiques
Heat resistant alloys
Metallography
Refractory materials
Periodicals
Electronic journals
669.73 - Journal URLs:
- http://www.sciencedirect.com/science/journal/02634368 ↗
http://www.elsevier.com/journals ↗ - DOI:
- 10.1016/j.ijrmhm.2019.105047 ↗
- Languages:
- English
- ISSNs:
- 0263-4368
- Deposit Type:
- Legaldeposit
- View Content:
- Available online (eLD content is only available in our Reading Rooms) ↗
- Physical Locations:
- British Library DSC - 4542.525420
British Library DSC - BLDSS-3PM
British Library HMNTS - ELD Digital store - Ingest File:
- 11828.xml