Impression creep deformation behaviour of 316LN stainless steel. (2nd November 2015)

• Record Type: Journal Article
• Authors: , Naveena; Shankar, Vani; Parameswaran, P.; Mathew, M.D.
• Is Part Of: Materials at high temperatures. Volume 32:Number 6(2015)
• Page Start: 583
• Page End: 591
• Publication Date: 2015-11-02
• Subjects: Plastic zone -- Impression creep -- 316LN SS -- Profilometry; Materials at high temperatures -- Periodicals; High temperatures -- Periodicals; 620.1121705
• DOI: 10.1179/1878641315Y.0000000004
• Languages: English
• ISSNs: 0960-3409

Abstract

Abstract : The impression creep deformation behaviour of 316LN SS was investigated from microstructure, substructure, microhardness and profilometry studies of the creep deformed region. Impression creep tests were conducted on 316LN SS in the temperature range of 923–973 K, at different punching stresses in the range of 472–760 MPa. The impression creep deformation was characterised by a hemispherically shaped plastic zone which developed around the indentation. The study revealed the distinct regions under the punch undergoing deformation to different extents. The deformation was found to occur predominently on (111) planes. The dislocations in the highly deformed region were well dispersed in the matrix. The size of the plastic zone was estimated to be ∼1·5 times the diameter of the indenter based on the microhardness and profilometry studies. The critical spacing to be maintained between the adjacent indentations was estimated to be >5 times the diameter of indenter.