Synthesis of ultrafine α-Al2O3 powder by two-step hydrolysis. Issue 4 (March 2018)

• Record Type: Journal Article
• Authors: Shi, Ruixia; Shang, Yaru; Zhang, Yan; Wang, Peng; Zhang, Aiyu; Yang, Ping
• Is Part Of: Ceramics international. Volume 44:Issue 4(2018)
• Page Start: 3741
• Page End: 3750
• Publication Date: 2018-03
• Subjects: Al2O3 -- Powders: chemical preparation -- Sol-gel processes -- Calcination; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2017.11.157
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: The ultrafine α-Al2 O3 powder has been successfully synthesized via two-step hydrolysis of aluminum isopropoxide. The effects of synthesis parameters on the α-Al2 O3 were investigated. The experimental results indicated that the concentration of aluminum isopropoxide, water bath temperature, the molar ratio of aluminum isopropoxide to isopropanol and aluminum isopropoxide to deionized water greatly affect the amount of nuclei and the microstructure of α-Al2 O3 . Additionally, the water bath temperature affects the rate of nucleation and growth of crystals. Transmission electron microscopy (TEM) images display that the well-dispersed α-Al2 O3 powder with particle size about 100 nm was obtained via the method after calcination at 1200 °C for 1 h. The coalescence of crystal particles led to the formation of vermicular α-Al2 O3 particles. The X-ray diffraction (XRD) and Fourier transform infrared spectra (FTIR) analysis demonstrated the possible phase transition process of α-Al2 O3 . The scanning electron microscopy (SEM) images of samples calcined at various temperatures showed the microstructure transformation. Brunauer-Emmett-Teller (BET) surface area and mean pore size of the samples varied with the calcination temperature. The addition of cetylrimethylammonium bromide (CTAB) has impacts on the phase transformation of α-Al2 O3 .