Functionalized MWCNTs modified flame retardant PLA nanocomposites and cold rolling process for improving mechanical properties. (16th June 2018)

• Record Type: Journal Article
• Authors: Gu, Liqiang; Qiu, Jianhui; Yao, Youwei; Sakai, Eiichi; Yang, Liting
• Is Part Of: Composites science and technology. Volume 161(2018)
• Page Start: 39
• Page End: 49
• Publication Date: 2018-06-16
• Subjects: Nano composites -- Synergism -- Mechanical properties -- Thermal properties -- Plastic deformation; Composite materials -- Periodicals; Composite materials; Fibrous composites; Periodicals; 620.118
• DOI: 10.1016/j.compscitech.2018.03.033
• Languages: English
• ISSNs: 0266-3538

Abstract

Abstract: 10-hydroxy-9, 10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO-OH) has been successfully covalently grafted onto the surfaces of multi-walled carbon nanotubes (MWCNTs) to obtain DOPO-functionalized MWCNTs (MWCNT-DOPO-OH) by a three-step process. The resultant core-shell nanostructured MWCNT-DOPO-OH was introduced into aluminum hypophosphite/poly(lactic acid) (AHP/PLA) flame retardant systems via melt blending to improve both flame retardancy and mechanical properties. AHP/PLA/MWCNT-DOPO-OH nanocomposites with synergistic effect of 1 wt.% MWCNT-DOPO-OH and 14 wt.% AHP were shown to be effective in improving flame retardancy with UL 94 V-0 rating and limiting oxygen index (LOI) value of 28.6. And these flame-retardant nanocomposites show a usable T g higher than 57.8 °C and much higher char yield for preventing the anti-dropping. Moreover, a cold rolling process was performed for AHP/PLA/MWCNT-DOPO-OH nanocomposites to further improve the mechanical properties for secondary processing. For 1 wt.% MWCNT-DOPO-OH loading PLA nanocomposites, the tensile strength increased from 69.5 MPa to 77.9 MPa and 82.0 MPa, and the fracture strain increased from 17.9% to 27.5% and 120%, at rolling ratios of 30% and 50%, respectively, indicating that MWCNT-DOPO-OH modified PLA was homogenized plastic deformation during the rolling process.