Corrosion products evolution and hot corrosion mechanisms of REPO4 (RE= Gd, Nd, La) in the presence of V2O5 + Na2SO4 molten salt. Issue 4 (April 2019)

• Record Type: Journal Article
• Authors: Guo, Lei; Zhang, Chenglong; He, Qing; Li, Zhihua; Yu, Jianxing; Liu, Xichun; Ye, Fuxing
• Is Part Of: Journal of the European Ceramic Society. Volume 39:Issue 4(2019)
• Page Start: 1496
• Page End: 1506
• Publication Date: 2019-04
• Subjects: Thermal barrier coatings -- REPO4 -- Hot corrosion -- V2O5+Na2SO4; Ceramic materials -- Periodicals; Composite materials -- Periodicals; Matériaux céramiques -- Périodiques; Composites -- Périodiques; Ceramic materials; Composite materials; Periodicals; Electronic journals; 666.05
• DOI: 10.1016/j.jeurceramsoc.2018.10.031
• Languages: English
• ISSNs: 0955-2219

Abstract

Abstract: REPO4 (RE = Gd, Nd, La) ceramics with a monazite structure were fabricated by a chemical co-precipitation and calcination method. Hot corrosion tests were carried out in V2 O5 +Na2 SO4 molten salt at 800 °C, 900 °C and 1000 °C for 2 h and 10 h. The temperature and heat duration had little effect on the type of corrosion products in this study. However, GdPO4 and REPO4 (RE = Nd, La) revealed different hot corrosion behavior. Exposed to the molten salt, GdVO4 and Gd4 (P2 O7 )3 formed as the corrosion products for the GdPO4 case, while an RE(P, V)O4 (RE = Nd, La) solid solution was generated for NdPO4 and LaPO4 cases. The formation of the solid solution had less damage to the original microstructure, which benefited the hot corrosion resistance of the ceramics. From the crystallographic characteristics of rare earth phosphates/vanadates and a thermodynamics perspective, the hot corrosion mechanisms of REPO4 (RE = Gd, Nd, La) are discussed.