Enhanced viscoelasticity of polyalphaolefins confined and sheared in submicron-to-nanometer-sized gap range and its dependence on shear rate and temperature. (April 2018)

• Record Type: Journal Article
• Authors: Itoh, Shintaro; Ohta, Yuya; Fukuzawa, Kenji; Zhang, Hedong
• Is Part Of: Tribology international. Volume 120(2018)
• Page Start: 210
• Page End: 217
• Publication Date: 2018-04
• Subjects: Micro-/nano-scale friction -- Lubrication oil -- Rheology -- Measurement; Tribology -- Periodicals; 621.89
• DOI: 10.1016/j.triboint.2017.12.022
• Languages: English
• ISSNs: 0301-679X

Abstract

Abstract: The viscoelasticity of polyalphaolefins confined and sheared in a submicron-to-nanometer-sized gap range was measured. A continuous transition from bulk viscosity to confined viscoelasticity was observed in this gap range. The viscosity increased when the gap was less than around 100 nm, whereas the elasticity rapidly increased when the gap was less than 10 nm. The shear rate and temperature dependence of the unique viscoelasticity was also measured in the confined state. The enhanced viscosity decreased as the shear rate and the temperature increased. These findings are expected to improve the basic understanding of hydrodynamic lubrication design in narrow gaps widths. Highlights: The viscoelasticity of polyalphaolefins confined in a small gap range was measured. A continuous transition from bulk viscosity to confined viscoelasticity was seen. The enhanced viscosity decreased as the shear rate and the temperature increased.