Evolution of fatigue crack growth and fracture behavior in gamma titanium aluminide Ti-43.5Al-4Nb-1Mo-0.1B (TNM) forgings. (June 2018)

• Record Type: Journal Article
• Authors: Dahar, Matthew S.; Tamirisakandala, Sesh A.; Lewandowski, John J.
• Is Part Of: International journal of fatigue. Volume 111(2018)
• Page Start: 54
• Page End: 69
• Publication Date: 2018-06
• Subjects: Gamma TiAl -- Gas turbines -- Crack growth rate -- Plastic zone -- Fractography; Materials -- Fatigue -- Periodicals; Materials -- Fatigue; Periodicals; 620.1122
• DOI: 10.1016/j.ijfatigue.2018.01.026
• Languages: English
• ISSNs: 0142-1123

Abstract

Highlights: Fatigue behavior very dependent on the material condition as well as load ratio, R. Forged tensile specimens show better properties then as-cast and as-cast + HIP. Crack growth rates do not coverage when plotted vs. Kmax suggesting effect of ΔK. Kmax at failure was not affected by load ratio, R and similar to pre-cracks samples. Abstract: The effects of thermal and thermomechanical processing, sample orientation, and load ratio on the room temperature fatigue crack growth and fracture behavior of a third-generation gamma titanium aluminide Ti-43.5Al-4Nb-1Mo-0.1B (TNM) were determined in this study. Bend bar specimens, excised from TNM in as-cast, cast + hot isostatic pressing, and forge + heat treat conditions in the longitudinal and transverse directions, were tested at room temperature in lab air. Load ratio in the range 0.1–0.9 was used in fatigue testing to determine its effect on the fatigue threshold, Paris regime, and stress intensity at overload. Microscopy, fractography, and X-ray diffraction were used to understand the effects of process and testing variables on the fatigue crack path and morphology. The effects of microstructure length scales and microconstituents are discussed in relation to the properties measured.