Influence of temperature on the high-cycle fatigue properties of compacted graphite iron. (July 2018)

• Record Type: Journal Article
• Authors: Qiu, Y.; Pang, J.C.; Zhang, M.X.; Zou, C.L.; Li, S.X.; Zhang, Z.F.
• Is Part Of: International journal of fatigue. Volume 112(2018)
• Page Start: 84
• Page End: 93
• Publication Date: 2018-07
• Subjects: Compacted graphite iron -- Fatigue properties -- Fatigue strength -- Fatigue damage mechanism; Materials -- Fatigue -- Periodicals; Materials -- Fatigue; Periodicals; 620.1122
• DOI: 10.1016/j.ijfatigue.2018.02.034
• Languages: English
• ISSNs: 0142-1123

Abstract

Highlights: The decreasing rate of fatigue strength increases above 400 °C. Fatigue strength coefficient and fatigue strength exponent perform inversely. Fatigue crack initiation is induced by the vermicular graphite debonding. Ferrite plastic deformation is from slip band to grain boundary sliding. Abstract: High-cycle fatigue tests of compacted graphite iron (CGI) at 25 °C, 400 °C and 500 °C were performed. The corresponding fatigue damage mechanisms were investigated by the observations on fractographies and longitudinal section morphologies of typical samples. The results show that the decreasing rate of fatigue strength from 400 °C to 500 °C is higher than that from 25 °C to 400 °C. The fatigue strength coefficient of S - N curve fitted with the Basquin relationship decreases from 25 °C to 400 °C and increases from 400 °C to 500 °C; while the fatigue strength exponent performs in an inverse tendency. These are resulted from plastic deformation mode transition of the ferrite at the tip of the crack induced by the graphite debonding: slip band at 25 °C and 400 °C to grain boundary sliding at 500 °C. Finally, the influences of carbide on fatigue properties were discussed.