MgB2 wire diameter reduction by hot isostatic pressing—a route for enhanced critical current density. (8th June 2018)

• Record Type: Journal Article
• Authors: Morawski, A; Cetner, T; Gajda, D; Zaleski, A J; Häßler, W; Nenkov, K; Rindfleisch, M A; Tomsic, M; Przysłupski, P
• Is Part Of: Superconductor science & technology. Volume 31:Number 7(2018:Jul.)
• Publication Date: 2018-06-08
• Subjects: superconductivity -- MgB -- wires -- hot isostatic pressing -- electrical connectivity; Superconductivity -- Periodicals; Superconductors -- Periodicals; 537.623
• DOI: 10.1088/1361-6668/aac55a
• Languages: English
• ISSNs: 0953-2048

Abstract

Abstract: The effect of wire diameter reduction on the critical current density of pristine MgB2 wire was studied. Wires were treated by a hot isostatic pressing method at 570 °C and at pressures of up to 1.1 GPa. It was found that the wire diameter reduction induces an increase of up to 70% in the mass density of the superconducting cores. This feature leads to increases in critical current, critical current density, and pinning force density. The magnitude and field dependence of the critical current density are related to both grain connectivity and structural defects, which act as effective pinning centers. High field transport properties were obtained without doping of the MgB2 phase. A critical current density jc of 3500 A mm −2 was reached at 4 K, 6 T for the best sample, which was a five-fold increase compared to MgB2 samples synthesized at ambient pressure.