Nitridation of grate in a biomass‐fired boiler. Issue 8 (2nd April 2019)

• Record Type: Journal Article
• Authors: Montgomery, Melanie; Dahl, Kristian V.; Grumsen, Flemming B.; Kværndrup, Frederik B.; Hald, John
• Is Part Of: Materials and corrosion. Volume 70:Issue 8(2019)
• Page Start: 1461
• Page End: 1475
• Publication Date: 2019-04-02
• Subjects: biomass boiler -- iron nitrides -- straw -- welding problems; Materials -- Periodicals; Metals -- Periodicals; Corrosion and anti-corrosives -- Periodicals; 620.1122305
• DOI: 10.1002/maco.201810630
• Languages: English
• ISSNs: 0947-5117

Abstract

Abstract: After a straw‐fired power plant in Denmark had been in operation for 16 years with 93, 815 hr operation, there was a need for overlay welding repair of the grate due to a decrease in wall thickness from erosion/corrosion. The grate consisted of 15Mo3 (Werkstoff nr. 1.5415) tubes where water/steam flows through, which were welded together with fins, and where one side faced the combustion zone coming into contact with the fuel (the side that required weld overlay). The water/steam temperature was 320°C and the surface metal temperature was estimated to be 350°C. However, there were difficulties when trying to overlay weld the grate as the weld pool was unstable. The microhardness measurements on cross‐sections of the tubes revealed a higher hardness of the tube facing the combustion zone compared to opposite the combustion zone. In addition, there was higher hardness adjacent to the combustion side than the steam/water side. Analysis of etched cross‐sections with light optical and scanning electron microscopy revealed the presence of acicular structures at the convex surface. Further analysis has been conducted with X‐ray diffraction and a LECO nitrogen analyser indicating the presence of iron nitrides. Reasons for their evolution and implications for the repair welding are discussed. Abstract : There were problems in repair welding of a biomass grate tube operating at 350°C for 16 years. Using various microscopy and analysis techniques, it was revealed that (a) FeOOH + Fe3 O4 was present as a corrosion product and (b) nitridation had occurred on the tube closest to the combustion zone where Fe4 N acicular phases were identified. This phase will be unstable during welding resulting in the release of nitrogen gas.