Facile fabrication of POSS-Modified MoS2/PMMA nanocomposites with enhanced thermal, mechanical and optical limiting properties. (8th September 2018) - Liao, Qiaobo
Abstract: A facile strategy was applied to transfer chemically exfoliated molybdenum disulphide (MoS2 ) nanosheets from aqueous medium to organic solvents. The MoS2 nanosheets were then modified by trisilanol-phenyl-POSS (T7 POSS) which was confirmed by Fourier transform infrared (FT-IR), X-ray photoelectron spectroscopy (XPS) and Powder X-Ray Diffraction (PXRD). The modified MoS2 nanosheets were then incorporated into poly (methyl methacrylate) (PMMA) via a simple solution blending method. The Scanning Electron Microscope (SEM) and Transmission electron microscope (TEM) were employed to demonstrate the well-dispersion of nanosheets in polymeric matrix. Compared to neat PMMA, the decomposition temperatures (Td ) and the half weight decomposition temperatures (Thalf ) of POSS-MoS2 /PMMA nanocomposites at nanosheets concentration of 0.2 wt% were dramatically increased by 35.2 °C and 35.3 °C, respectively. Meanwhile, according to the measurements of Dynamic Mechanical Analysis (DMA), the storage modulus at 30 °C is significantly improved by 5.2 times and the glass transition temperature (Tg ) is also enhanced by 6.2 °C. Remarkably, POSS-MoS2 /PMMA nanocomposites possess low optical limiting differential transmittance Tc (0.5%), low nonlinear optical absorption onset threshold FON (0.02 J⋅cm −2 ), low optical limiting threshold FOL (0.4 J⋅cm −2 ) and high nonlinear coefficient β (297⋅cm GW −1 ), highlighting their vast potential in the development of solid-state optical limiting materials.