Environmentally friendly synthesis of photoluminescent biochar dots from waste soy residues for rapid monitoring of potentially toxic elements. Issue 38 (12th July 2019) - Zhang, Liting
Abstract : Waste biomass was used as a carbon precursor to prepare photoluminescent biochar dots for economical and eco-friendly monitoring of Hg 2+ and Fe 3+ ions. Abstract : Single-step environmentally friendly synthesis of biochar dots (BCDs) was developed using hydrothermal treatment of waste biomass. Using soy residue as the carbon precursor, the resultant BCDs had strong and stable photoluminescence. Characterization by atomic force microscopy (AFM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and infrared spectroscopy indicates that the BCDs prepared were water soluble, spherical, oxygenous and nitrogen-doped carbon nanoparticles with 10–20 nm in diameter. The fluorescence quantum yield of the BCDs was 3.7%. The use of the BCDs as a very effective fluorescent probe for label-free, rapid, and selective detection of Hg 2+ and Fe 3+ ions was further demonstrated with good linear relationships at 0–50 μM and 10–50 μM, respectively. The minimum detection limits of Hg 2+ and Fe 3+ were 100 nM and 30 nM. Furthermore, the feasibility of using the BCDs for monitoring of Hg 2+ and Fe 3+ in open waters was also established.