Failure analysis of steam jet pump at top of crude oil vacuum distillation tower. (September 2019)

• Record Type: Journal Article
• Authors: Tian, Jisheng; Wang, Lida; Sun, Wen; Yang, Yong; Liu, Zhimei; Wang, Guangzhou; Zhao, Liqiu; Zhou, Yingzheng; Liu, Guichang
• Is Part Of: Engineering failure analysis. Volume 103(2019)
• Page Start: 9
• Page End: 19
• Publication Date: 2019-09
• Subjects: Steam jet pump -- Failure -- CFD simulation -- Erosion -- Selective corrosion; System failures (Engineering) -- Periodicals; Fracture mechanics -- Periodicals; Reliability (Engineering) -- Periodicals; Pannes -- Périodiques; Rupture, Mécanique de la -- Périodiques; Fiabilité -- Périodiques; Fracture mechanics; Reliability (Engineering); System failures (Engineering); Periodicals; Electronic journals; 620.112
• DOI: 10.1016/j.engfailanal.2019.04.024
• Languages: English
• ISSNs: 1350-6307

Abstract

Abstract: The steam jet pump made by SAF 2205 duplex stainless steel (DSS) provides vacuum for vacuum distillation tower to improve the distillation efficiency of crude oil. The pump suffers from severe local wall thinning during service, especially at diffuser section. Failure analysis of the pump is carried out using traditional characterization techniques and computational fluid dynamics (CFD) simulation. The results show that the pump suffer from not only the electrochemical corrosion of acidic droplets forming in HCl-H2 S-H2 O environment, but also the mechanical erosion by high speed flow with a large value of wall shear stress. A vicious erosion-corrosion circle built by electrochemical corrosion together with mechanical erosion leads to severe damage at the diffuser section of steam jet pump. Highlights: Steam jet pump on top of crude oil vacuum distillation tower fails during service. Failure analysis is carried out using experimental techniques and fluid simulation. The pump suffers from severe mechanical erosion induced by high speed flow. A vicious erosion-corrosion circle accelerates local thinning of the pump wall.