High-temperature wettability and interactions between NbSi-based alloys and Y2O3 ceramics. Issue 1 (January 2018)

• Record Type: Journal Article
• Authors: Wan, Beibei; Zhang, Huarui; Ran, Chao; Bai, Peng; Zhang, Hu
• Is Part Of: Ceramics international. Volume 44:Issue 1(2018)
• Page Start: 32
• Page End: 39
• Publication Date: 2018-01
• Subjects: High-temperature wettability -- Yttria -- NbSi-based alloys -- Interfacial interaction; Ceramics -- Periodicals; Céramique industrielle -- Périodiques; Ceramics; Periodicals; Electronic journals; 666
• DOI: 10.1016/j.ceramint.2017.07.163
• Languages: English
• ISSNs: 0272-8842

Abstract

Abstract: The high-temperature wettability and interactions between NbSi-based alloys and Y2 O3 ceramics with various microstructures were studied, based on which the corresponding mechanisms were discussed. The results showed that there was a characteristic transition during the high temperature wetting between the alloys and ceramics when the Y2 O3 microstructure changed. The rate of spreading of molten NbSi-based alloys on the Y2 O3 ceramics was relatively high when the level of open porosity was greater than 20.8%. As the level of open porosity of the Y2 O3 ceramics increased from 6.9% to 27.8%, the initial and equilibrium contact angles between the alloys and ceramics increased from 81.3° to 110.0°, and from 60.5° to 93.2°, respectively. TiO and Ti2 O phases formed within the alloy matrix of each wetting system. However, as the level of open porosity of the Y2 O3 substrates increased, the Ti-oxide content initially gradually decreased and subsequently increased. The alloy in the system with the open porosity level of 20.8% contained the lowest Ti-oxide content while the system with the open porosity level of 6.9% contained the most.