Characterization and Evaluation of the Improved Performance of Modified Reverse Osmosis Membranes by Incorporation of Various Organic Modifiers and SnO2 Nanoparticles. (21st June 2015)

• Record Type: Journal Article
• Authors: AL-Sheetan, Kh. M.; Shaik, Mohammed Rafi; AL-Hobaib, A. S.; Alandis, N. M.
• Other Names: Torrisi Vanna Academic Editor.
• Is Part Of: Journal of nanomaterials. Volume 2015(2015)
• Publication Date: 2015-06-21
• Subjects: Nanostructured materials -- Periodicals; Nanotechnology -- Periodicals; Nanomatériaux; Nanostructured materials; Nanotechnology; Nanostructures; Nanotechnology; Periodicals; Fulltext; Internet Resources; Periodicals; 620.115
• DOI: 10.1155/2015/363175
• Languages: English
• ISSNs: 1687-4110

Abstract

Abstract : Reverse osmosis (RO) membranes modified withSnO 2 nanoparticles of varied concentrations (0.001–0.1 wt.%) were developed via in situ interfacial polymerization (IP) of trimesoyl chloride (TMC) and m -phenylenediamine (MPD) on nanoporous polysulfone supports. The nanoparticles dispersed in the dense nodular polyamide on the polysulfone side. The effects of IP reaction time andSnO 2 loading on membrane separation performance were studied. The modified reverse osmosis membranes were characterized by scanning electron microscopy (SEM), X-ray diffractometer (XRD), energy dispersive X-ray spectroscopy (EDX), transmission electron microscopy (TEM), contact angle measurement, and atomic force microscopy (AFM). The synthesizedSnO 2 nanoparticles size varies between 10 and 30 nm. The results exhibited a smooth membrane surface and average surface roughness from 31 to 68 nm. Moreover, hydrophilicity was enhanced and contact angle decreased. The outcomes showed that an IP reaction time was essential to form a denserSnO 2 -polyamide layer for higher salt rejection, the developed reverse osmosis membranes with the incorporation of theSnO 2 nanoparticles were examined by measuring permeate fluxes and salt rejection, and the permeate flux increased from 26 to 43.4 L/m 2 ·h, while salt rejection was high at 98% (2000 ppm NaCl solution at 225 psi (1.55 MPa), 25°C).