Nanoporous Calcium Silicate and PLGA Biocomposite for Bone Repair. (8th September 2010)

• Record Type: Journal Article
• Authors: Su, Jiacan; Wang, Zhiwei; Yan, Yonggang; Wu, Yongfa; Cao, Liehu; Ma, Yuhai; Yu, Baoqing; Li, Ming
• Other Names: Gu Hongchen Chen Academic Editor.
• Is Part Of: Journal of nanomaterials. Volume 2010(2010)
• Publication Date: 2010-09-08
• Subjects: Nanostructured materials -- Periodicals; Nanotechnology -- Periodicals; Nanomatériaux; Nanostructured materials; Nanotechnology; Nanostructures; Nanotechnology; Periodicals; Fulltext; Internet Resources; Periodicals; 620.115
• DOI: 10.1155/2010/181429
• Languages: English
• ISSNs: 1687-4110

Abstract

Abstract : Nanoporous calcium silicate (n-CS) with high surface area was synthesized using the mixed surfactants of EO 20 PO 70 EO 20 (polyethylene oxide) 20 (polypropylene oxide) 70 (polyethylene oxide) 20, P123) and hexadecyltrimethyl ammonium bromide (CTAB) as templates, and its composite with poly(lactic acid-co-glycolic acid) (PLGA) were fabricated. The results showed that the n-CS/PLGA composite (n-CPC) with 20 wt% n-CS could induce a dense and continuous layer of apatite on its surface after soaking in simulated body fluid (SBF) for 1 week, suggesting the excellent in vitro bioactivity. The n-CPC could promote cell attachment on its surfaces. In addition, the proliferation ratio of MG 63 cells on n-CPC was significantly higher than PLGA; the results demonstrated that n-CPC had excellent cytocompatibility. We prepared n-CPC scaffolds that contained open and interconnected macropores ranging in size from 200 to 500 μ m. The n-CPC scaffolds were implanted in femur bone defect of rabbits, and the in vivo biocompatibility and osteogenicity of the scaffolds were investigated. The results indicated that n-CPC scaffolds exhibited good biocompatibility, degradability, and osteogenesis in vivo. Collectively, these results suggested that the incorporation of n-CS in PLGA produced biocomposites with improved bioactivity and biocompatibility.