Corrosion at the carbon steel-clay compact interface at 90°C: Insight into short- and long-term corrosion aspects. (15th May 2019)

• Record Type: Journal Article
• Authors: Schlegel, M.L.; Martin, F.; Fenart, M.; Blanc, C.; Varlet, J.; Foy, E.; Prêt, D.; Trcera, N.
• Is Part Of: Corrosion science. Volume 152(2019)
• Page Start: 31
• Page End: 44
• Publication Date: 2019-05-15
• Subjects: Carbon steel (A) -- Clay (A) -- SEM (B) -- XRD (B) -- Raman spectroscopy (B); Corrosion and anti-corrosives -- Periodicals; 620.11223
• DOI: 10.1016/j.corsci.2019.01.027
• Languages: English
• ISSNs: 0010-938X

Abstract

Highlights: Carbon steel was corroded in contact with anoxic clay at 90 °C. Corrosion damage equaled 8.5 and 29.5 μm at 7 and 76 months, respectively. Heterogeneous corrosion with Fe silicate, ankerite or akaganeite at 7 months. Comparable interfaces contain Fe silicate, chukanovite, sulfide for 15–76 months. Long-term generalized corrosion approximated by a linear law. Abstract: Rods of low alloy carbon steel were corroded under anoxic conditions in compact clay at 90 °C. Gravimetrically-assessed corrosion damage equalled 8.5 μm at 7 months, then slowly increased to 29.5 μm at 76 months. The corrosion damage was heterogeneous at 7 months, and two distinct aspects coexisted: steel was replaced by (Fe, Si, O) corrosion products in some areas, and by Si-poor hydroxide and covered by akaganeite (FeO(OH, Cl)) in others, indicating corrosion in suboxic conditions. A magnetite fringe contacted the steel surface. For greater reaction times, akaganeite disappeared, and only (Fe, Si, O) corrosion products containing Fe sulfide and chukanovite were detected.