Controlling the wettability and adhesion of carbon fibers with polymer interfaces via grafted nanofibers. (29th September 2015)

• Record Type: Journal Article
• Authors: Hong, Seokjin; Minary-Jolandan, Majid; Naraghi, Mohammad
• Is Part Of: Composites science and technology. Volume 117(2015)
• Page Start: 130
• Page End: 138
• Publication Date: 2015-09-29
• Subjects: Hybrid composites -- Polymer-matrix composites (PMCs) -- Interface -- Electro-spinning -- Fiber/matrix bond; Composite materials -- Periodicals; Composite materials; Fibrous composites; Periodicals; 620.118
• DOI: 10.1016/j.compscitech.2015.06.008
• Languages: English
• ISSNs: 0266-3538

Abstract

Abstract: Interfacial properties in carbon fiber composites is one of the key parameters controlling their structural functionality. Here, we introduce a novel method to engineer carbon fiber-epoxy interfaces, via inclusion of nanofibers, towards higher interfacial strength and energy dissipation. In our method, thermally stabilized polyacrylonitrile (PAN) nanofibers are grafted onto carbon fibers via electro-spinning process, followed by nanofiber consolidation via solvent vapor and thermal treatment. These treatments partially dissolves nanofibers along the nanofiber-fiber interface and trigger entropic elasticity in nanofibers, thus, increasing the nanofiber-fiber interactions. The hybridization of carbon fibers with PAN nanofibers increased the interfacial shear strength (IFSS) by ∼48%, from 10.8 ± 2.6 to 15.9 ± 4.9 MPa. Postmortem fractography points to mechanical interlocking between nanofibers and epoxy and reinforcing effects of nanofibers in matrix as root causes of IFSS enhancement. As a result of adding nanofibers to carbon fiber, junction failure mode changes from a dominantly adhesive failure (at epoxy-fiber interface) to dominantly cohesive failure, and failure plane slightly shifts away from epoxy-fiber interface to within the epoxy. Compared to other types of whiskers grown on carbon fibers, such as CNTs, the method proposed here requires low temperatures (below 300 °C), during which no surface damages are expected to accumulate on carbon fibers.