Interaction between phase transformations and dislocations at the nanoscale. Part 2: Phase field simulation examples. (September 2015)

• Record Type: Journal Article
• Authors: Javanbakht, Mahdi; Levitas, Valery I.
• Is Part Of: Journal of the mechanics and physics of solids. Volume 82(2015:Sep.)
• Page Start: 164
• Page End: 185
• Publication Date: 2015-09
• Subjects: Phase field approach -- Phase transformation -- Dislocations -- Large strains -- Inheritance of dislocations -- Finite element simulations; Mechanics, Applied -- Periodicals; Solids -- Periodicals; Mechanics -- Periodicals; Mécanique appliquée -- Périodiques; Solides -- Périodiques; Mechanics, Applied; Solids; Periodicals; 531.05
• DOI: 10.1016/j.jmps.2015.05.006
• Languages: English
• ISSNs: 0022-5096

Abstract

Abstract: The complete system of phase field equations for coupled martensitic phase transformations (PTs), dislocation evolution, and mechanics at large strains is presented. Finite element method (FEM) is utilized to solve this system for two important problems. The first one is related to the simulation of shear strain-induced PT at the evolving dislocation pile-ups in a nanosized bicrystal. Plasticity plays a dual part in the interaction with PT. Dislocation pile-ups produce strong stress tensor concentrators that lead to barrierless martensite (M ) nucleation. On the other hand, plasticity in the transforming grain relaxes these stress concentrators suppressing PT. The final stationaryM morphology is governed by the local thermodynamic equilibrium, either at the interfaces or in terms of stresses averaged over the martensitic region or the entire grain. This is very surprising because of strong heterogeneity of stress fields and is in contrast to previous statements that phase equilibrium conditions do not enter the description of strain-induced PTs. The second problem is devoted to martensitic plate propagation through a bicrystal during temperature-induced PT. For elastic growth (without dislocations) and a large thermal driving force, a complex transformation path with plate branching and direct and reverse PTs is observed, which still ends with the same stationary nanostructure as for a smaller driving force and a traditional transformation path. Sharp grain boundary arrests plate growth at a relatively small driving force, exhibiting an athermal friction. For elastoplastic growth, the generation of dislocations produces athermal friction and arrests the plate below some critical driving force, leading to a morphological transition from plate to lathM . The width of the martensitic plate increases in comparison with elastic growth due to internal stress relaxation. Plate growth is accompanied by the nucleation of dislocations withinM and remaining inM, the nucleation of dislocations at the tip of a plate and spreading them in austenite (A ), and passing some dislocations throughM, then through aM -A interface, and then throughA . Due to the existence of a stationary equilibriumM nanostructure and concentration for each temperature, for a large enough observation time one observes athermal, rate- and time-independent kinetics, even while local kinetics is rate dependent. In the final structure, most dislocations are inM despite its having a yield strength three times larger than forA, which is consistent with experiments.