Synthesis, crystal structure and magnetic properties of iron oxides nanoparticles for biomedical applications. (8th October 2010)

• Record Type: Journal Article
• Authors: Rashdan, S.; Bououdina, M.; Al-Saie, A.; Ghanem, E.; Bin-Thani, A.; Althawadi, S.
• Is Part Of: International journal of nanoparticles. Volume 3:Number 3(2010)
• Page Start: 220
• Page End: 228
• Publication Date: 2010-10-08
• Subjects: magnetic nanoparticles -- co-precipitation method -- oxidative hydrolysis method -- X-ray diffraction -- magnetic properties -- synthesis -- crystal structure -- iron oxides -- biomedical applications -- nanotechnology; Nanotechnology -- Periodicals; 620.505
• Languages: English
• ISSNs: 1753-2507

Abstract

Magnetic Fe3O4 nanoparticles have been synthesised by two methods: co-precipitation using a range of Fe3+ and Fe27+ raw materials; oxidative hydrolysis using various Fe2+ salts. X-ray diffraction analysis shows that most of the samples prepared by the co-precipitation method resulted in a mixture of two iron oxide phases (Fe2O3 and Fe3O4) with the presence of impurities (unreacted precursors) while using the oxidative hydrolysis method, Fe3O4 was found to be a major product. Magnetic measurements confirm the results obtained by X-ray diffraction. The sample prepared using FeSO4 as precursor in urea and PEG 200 at 40-50°C for 3 hours (nominated as E2) gives an average crystallites size around 70 nm, a saturation magnetisation Ms = 75 emu/g, a remanence of Mr = 12 emu/g and a coercivity of Hc = 110 kOe, which can be a good candidate for biomedical applications.