Chemical state changes of Nafion in model polymer electrolyte fuel cell under oxygen/hydrogen gas atmosphere observed by S-K XANES spectroscopy. Issue 67 (14th November 2018)

• Record Type: Journal Article
• Authors: Isegawa, Kazuhisa; Kim, Daehyun; Kondoh, Hiroshi
• Is Part Of: RSC advances. Volume 8:Issue 67(2018)
• Page Start: 38204
• Page End: 38209
• Publication Date: 2018-11-14
• Subjects: Chemistry -- Periodicals; 540.5
• DOI: 10.1039/c8ra06426a
• Languages: English
• ISSNs: 2046-2069

Abstract

Abstract : Behavior of sulfur species derived from Nafion in PEFC under oxygen atmosphere was revealed by S-K XANES spectroscopy. Abstract : Changes in the chemical states of the sulfonic groups of Nafion in a model polymer electrolyte fuel cell under an oxygen/hydrogen gas atmosphere were studied using sulfur K-edge XANES spectroscopy. First, the chemical state changes in the sulfonic acid groups of both cathode and anode electrodes due to humidity under oxygen/hydrogen gas flow were observed. Reversible spectral changes ascribed to the hydration and dehydration of the sulfonic acid group were observed at both electrodes. This result is similar to the experimental results obtained without introducing oxygen (helium/hydrogen). On the anode, some of the sulfonic acid groups were decomposed to atomic sulfur adsorbed on platinum (Sad ) and the amount increased with time. On the cathode, the formation of Sad was suppressed under the oxygen atmosphere. Next, the effects of oxygen gas introduction onto Sad were examined. Sad was at once formed on both electrodes under dry conditions without an oxygen supply. By supplying oxygen gas, Sad on the cathode disappears. Therefore, the catalyst of the cathode has the ability to recover against the poisoning Sad, while that on the anode accumulates.