A critical assessment of multifunctional polymers with regard to their potential use in structural applications. (15th January 2019)

• Record Type: Journal Article
• Authors: Polydoropoulou, P.V.; Katsiropoulos, Ch.V.; Pantelakis, Sp.G.; Raimondo, M.; Guadagno, L.
• Is Part Of: Composites. Number 157(2019)
• Page Start: 150
• Page End: 162
• Publication Date: 2019-01-15
• Subjects: Thermosetting resin -- Electron microscopy -- Mechanical testing -- Particle-reinforcement -- Polyhedral oligomeric silsesquioxanes (POSS); Composite materials -- Periodicals; Materials science -- Periodicals; Composite materials; Periodicals; Electronic journals; 620.118
• DOI: 10.1016/j.compositesb.2018.08.092
• Languages: English
• ISSNs: 1359-8368

Abstract

Abstract: Multi Wall Carbon Nanotubes (MWCNTs) and Polyhedral Oligomeric Silsesquioxanes (POSS) are common additives to simultaneously enhance electrical conductivity and flame resistance. In the present work, the synergistic effect of the addition of MWCNTs and two different POSS compounds, DodecaPhenyl POSS (DPHPOSS) and Glycidyl POSS (GPOSS), on the mechanical behavior of multifunctional polymers subjected both to quasi-static as well as to fatigue loading was investigated. The results of the mechanical tests were discussed supported by Scanning Electron Microscope (SEM) and Energy Dispersive Spectroscopy (EDS) analyses. The results showed that the incorporation of MWCNTs in the resin containing GPOSS determines a slight decrease in the flexural modulus compared to the unfilled resin. The material filled with MWCNTs and DPHPOSS shows a higher reduction of the flexural modulus as compared to the other analyzed materials. The same trend was observed also for the flexural strength; more than 50% decrease of the flexural strength of the material filled with MWCNTs and DPHPOSS is detected. As far as the fatigue is concerned, it seems that the incorporation of the flame retardants led to an appreciable decrease in the fatigue life. The decrease in the mechanical properties of the nanofilled resin loaded with DPHPOSS is most likely due to the presence of aggregates of DPHPOSS crystals in the matrix. This hypothesis is confirmed by EDX analysis which shows that DPHPOSS forms some small aggregates, whereas GPOSS, being molecularly solubilized in the epoxy formulation, shows mechanical performance more similar to the sample loaded only with carbon nanotubes.