Microstructural evolution of TiAl-based alloys deformed by high-pressure torsion. (1st October 2015)

• Record Type: Journal Article
• Authors: Cao, G.H.; Russell, A.M.; Oertel, C.-G.; Skrotzki, W.
• Is Part Of: Acta materialia. Volume 98(2015)
• Page Start: 103
• Page End: 112
• Publication Date: 2015-10-01
• Subjects: Titanium aluminides -- High-pressure torsion -- Microstructure -- Dislocations -- Transmission electron microscopy (TEM); Materials -- Periodicals; Materials science -- Periodicals; Materials -- Mechanical properties -- Periodicals; Metallurgy -- Periodicals; Chemistry, Inorganic -- Periodicals; 620.112
• DOI: 10.1016/j.actamat.2015.07.012
• Languages: English
• ISSNs: 1359-6454

Abstract

Graphical abstract: Abstract: A Ti-45Al-4(Cr, Nb, Ta, B) alloy was deformed by torsion in a Paterson-type rock deformation machine at 900 and 1000 °C under 400 MPa hydrostatic pressure. The development of the microstructure during high-pressure torsion (HPT) was studied by transmission electron microscopy (TEM). TEM investigations indicated that α2 -Ti3 Al transformed to γ-TiAl via intermediate Ti2 Al or Ti1.4 Al phases. The hexagonal Ti2 Al coexists with α2 -phase precipitates as platelets and globular morphology at domain boundaries and within the grain interior of the γ phase preferentially on dislocations. TEM examination revealed that the Burgers vectors of dislocations in torsion-deformed specimens were 1/2<1 1 0] and 1/2<1 1 2]. The α2 → γ transformation induced by torsion is a diffusional process, and the γ-phase growth occurs by a diffusion-controlled step mechanism. The grain size produced by HPT does not change significantly compared to the initial microstructure, which is at the micrometer-scale. During torsion a steady-state stage was achieved, and the power law stress exponents and activation energies were measured to be 1.77 and 1.42, and 3.45 and 3.37 eV for torsion deformed at 900 and 1000 °C, respectively. It is concluded that torsion deformation occurred by superplastic flow through grain-boundary sliding accommodated by dislocation motion.