Kinetics during hydrothermal synthesis of nanosized KxNa1−xNbO3. Issue 42 (11th October 2018)

• Record Type: Journal Article
• Authors: Skjærvø, Susanne Linn; Wells, Kristin H.; van Beek, Wouter; Grande, Tor; Einarsrud, Mari-Ann
• Is Part Of: CrystEngComm. Volume 20:Issue 42(2018)
• Page Start: 6795
• Page End: 6802
• Publication Date: 2018-10-11
• Subjects: Crystals -- Periodicals; Crystal growth -- Periodicals; Crystallography -- Periodicals; Cristaux -- Périodiques; Cristaux -- Croissance -- Périodiques; Cristallographie -- Périodiques; 548
• DOI: 10.1039/c8ce01178h
• Languages: English
• ISSNs: 1466-8033

Abstract

Abstract : In situ techniques are powerful for providing insight into the determining factors when preparing K x Na1− x NbO3 nanoparticles with a designed composition, structure and size. Abstract : Hydrothermal synthesis is an efficient method of making nanosized functional oxide materials, and it has also been used to synthesize K x Na1− x NbO3 solid solution, a promising lead-free piezoelectric material. However, the control of nucleation and growth during synthesis to tailor the properties of materials is challenging and this work aimed to solve the challenges reported regarding the stoichiometry and size of K x Na1− x NbO3 formed by hydrothermal synthesis by in situ X-ray diffraction. K x Na1− x NbO3 crystallites of 18–65 nm with a controlled stoichiometry were produced by varying the Na/K ratio in the precursor solution, the solvent type and the final reaction temperature. The reaction proceeds via rapid formation of a potassium sodium hexaniobate intermediate phase during heating, which converts to K x Na1− x NbO3 at the reaction temperature. The Na occupancy in K x Na1− x NbO3 was found to correlate with the Na content in the intermediate phase and decreases by using a mix of ethanol and water as a solvent instead of only water. We show that in situ techniques are powerful for providing insight into the determining factors when preparing oxide nanoparticles with a designed composition, structure and size.