Influence of surface and internal casting defects on the fatigue behaviour of A357-T6 cast aluminium alloy. (January 2016)

• Record Type: Journal Article
• Authors: Serrano-Munoz, I.; Buffiere, J.-Y.; Verdu, C.; Gaillard, Y.; Mu, P.; Nadot, Y.
• Is Part Of: International journal of fatigue. Volume 82:Part 3(2016)
• Page Start: 361
• Page End: 370
• Publication Date: 2016-01
• Subjects: A357-T6 cast aluminium alloy -- Internal defects -- Environmental conditions -- HCF -- Fractographic observations; Materials -- Fatigue -- Periodicals; Materials -- Fatigue; Periodicals; 620.1122
• DOI: 10.1016/j.ijfatigue.2015.07.032
• Languages: English
• ISSNs: 0142-1123

Abstract

Highlights: Artificial defects of ∅ ≈ 2 mm were used to induce internal failure. The internal defects induce similar fatigue lives to those of a defect-free material. These defects reduce fatigue life when placed at the free surface. Placing the defects at the surface and cycling in vacuum does not reduce fatigue live. Abstract: The influence of internal casting defects on the fatigue properties of A357-T6 alloy has been studied. Specimens with artificial casting defects ( ∅ eq ≈ 2 mm) placed at the surface or in the bulk have been produced. A reference S–N curve has been obtained for the material containing only natural defects (microshrinkages). Cycling has been performed in air or under vacuum. In spite of their relatively large size, the internal artificial defects do not induce a reduction of the fatigue life compared to the reference material. When the artificial defects are placed at the surface, a decrease is observed when the specimens are cycled in air but it disappears again when cycling is performed in vacuum conditions. The detrimental effect of the casting defects is discussed in relation to their ability to initiate a crack growing in vacuum or not. It can be concluded that the increased fatigue lives observed for internal defects are the consequence of slower crack initiation and propagation mechanism occurring in vacuum.