Laser processing of in situ TiN/Ti composite coating on titanium. (January 2016)

• Record Type: Journal Article
• Authors: Sahasrabudhe, Himanshu; Soderlind, Julie; Bandyopadhyay, Amit
• Is Part Of: Journal of the mechanical behavior of biomedical materials. Volume 53(2016)
• Page Start: 239
• Page End: 249
• Publication Date: 2016-01
• Subjects: Laser processing -- Ti nitride -- Wear resistance -- Hard coatings -- Surface modification; Biomedical materials -- Periodicals; Biomedical materials -- Mechanical properties -- Periodicals; Biomedical materials; Biomedical materials -- Mechanical properties; Periodicals; Electronic journals; 610.28
• DOI: 10.1016/j.jmbbm.2015.08.013
• Languages: English
• ISSNs: 1751-6161

Abstract

Abstract: Laser remelting of commercially pure titanium (CP-Ti) surface was done in a nitrogen rich inert atmosphere to form in situ TiN/Ti composite coating. Laser surface remelting was performed at two different laser powers of 425 W and 475 W. At each power, samples were fabricated with one or two laser scans. The resultant material was a nitride rich in situ coating that was created on the surface. The cross sections revealed a graded microstructure. There was presence of nitride rich dendrites dispersed in α-Ti matrix at the uppermost region. The structure gradually changed with lesser dendrites and more heat affected α-Ti phase maintaining a smooth interface. With increasing laser power, the dendrites appeared to be larger in size. Samples with two laser scans showed discontinuous dendrites and more α-Ti phase as compared to the samples with one laser scan. The resultant composite of TiN along with Ti2 N in α-Ti showed substantially higher hardness and wear resistance than the untreated CP-Ti substrate. Coefficient of friction was also found to reduce due to surface nitridation. Leaching of Ti 4+ ions during wear test in DI water medium was found to reduce due to laser surface nitriding. Highlights: Laser remelting of Ti in LENS allows for site specific surface modification. Metal ion release can be lowered by modifying Ti surface due to hard coating. Laser remelting resulted high hardness, excellent wear resistance and low COF.